Sensor with improved shelf life

ABSTRACT

The present invention provides a metal electrode stabilised by a coating, the coating comprising a sulfur containing moiety in its molecular structure. The coating may also include a hydrophilic group and a spacer between the sulfur containing moiety and the hydrophilic group. Preferably, the sulphur-containing moiety is selected from the group comprising thiol, disulphide and SOx, and the hydrophilic group is selected from the group comprising hydroxyl, amine, carboxyl, carbonyl, oligo (ethylene oxide) chain, and zwitterionic species. Compounds useful in the present invention include 2-mercaptoethanol, 2-mercaptoethylamine, 3-mercaptopropionic acid, thiophene, 4-carboxythiophene, cysteine, homocysteine, and cystine.

RELATED APPLICATIONS

[0001] This application is a continuation of PCT Application No. PCT/AU99/00166, filed on Mar. 16, 1999, which claimed priority from Australian Application No. PP 2503, filed on Mar. 20, 1998.

TECHNICAL FIELD

[0002] The invention relates to apparatus comprising one or more metal electrodes such as electrochemical cells, sensor elements and the like, and more particularly to extending the shelf life of such apparatus.

BACKGROUND ART

[0003] Metal electrodes have proved useful in sensor elements for sensing a diverse range of biologically important molecules eg glucose, and for determining physical properties such as pH. A range of possible configurations and applications involving metal electrodes are discussed in our co-pending applications PCT/AU96/00210, PCT/AU96/00365 and PCT/AU96/00723.

[0004] A desirable attribute of all sensor elements is that they have a long shelf life—that is, the sensing characteristic of the sensor element does not change significantly between manufacture and use (ie on storage).

[0005] In an electrochemical sensor element the stability of the electrode is critical to the stability of the sensor as a whole. Typically, when left to stand for long periods of time, electrodes become prone to instability in subsequent use thus limiting the useful shelf life. It is thought that such instability is caused by absorption or reaction of the metallic surface with atmospheric contaminants. It has also been observed that filling time of sensors deteriorates on prolonged storage.

[0006] It is an object of the present invention to overcome or ameliorate at least some of the above disadvantages in the prior art.

[0007] Surprisingly, the present applicant has found that by coating a metal electrode with a monolayer or multilayer of selected materials, electrode behavior can be significantly stabilised in comparison with uncoated metal electrodes without loss of the desirable sensing characteristics of the electrodes.

DESCRIPTION OF THE INVENTION

[0008] According to a first aspect, the invention consists in a metal electrode stabilised by a coating, said coating comprising a sulfur containing moiety in its molecular structure, said coating increasing the temporal stability of the electrode relative to a corresponding uncoated metal electrode without modifying other electrochemical properties of said metal electrode. “Comprising” as herein used is used in an inclusive sense, that is to say in the sense of but not limited to “including” or “containing”. The term is not intended in an exclusive sense (“consisting of” or “composed of”).

[0009] Preferably, the sulphur-containing moiety is selected from the group comprising thiol, disulphide and SO_(x) Most preferably the sulphur-containing moiety is a disulphide. The sulphur-containing moiety may also be incorporated in a cyclic structure.

[0010] According to a second aspect, the invention consists in a metal electrode stabilised by a coating according to the first aspect, further comprising a hydrophilic group in its molecular structure.

[0011] Preferably, the hydrophilic group is selected from the group comprising hydroxyl, amine, carboxyl, carbonyl, oligo (ethylene oxide) chain, and zwitterionic species. Most preferably, the hydrophilic group is a zwitterionic species. The most preferred zwitterionic species comprises an amine and a carboxyl group in proximity.

[0012] According to a third aspect, the invention consists in a metal electrode stabilised by a coating according to the second aspect, further comprising a spacer between the sulphur-containing moiety and the hydrophilic group.

[0013] Preferably, in the third aspect, the spacer consists of an alkyl group or an aromatic group. It is preferable that methylene or ethylene groups be included in the spacer element.

[0014] According to a fourth aspect, the invention consists in a method of preparing a metal electrode stabilised by a coating, comprising the step of contacting a metal electrode with a substance comprising a sulphur-containing moiety in its molecular structure.

[0015] According to a fifth aspect, the invention consists in a method of preparing a metal electrode stabilised by a coating, comprising the steps of contacting a metal electrode with a substance comprising a sulphur-containing moiety and a hydrophilic group in its molecular structure.

[0016] According to a sixth aspect, the invention consists in a method of preparing a metal electrode stabilised by a coating comprising the steps of contacting a metal electrode with a substance comprising a sulphur-containing moiety, a hydrophilic group and a spacer between the sulphur-containing moiety and the hydrophilic group in its molecular structure.

[0017] The preferred substances for use in the methods described in the fourth, fifth and sixth aspects are identical to those substances described in respect of the first, second and third aspects.

[0018] The invention also consists in a method of sensing an analyte, comprising the step of substituting the electrode in a known sensor device with a metal electrode stabilised by a coating according to the present invention, and sensing an analyte.

BEST MODE FOR CARRYING OUT THE INVENTION

[0019] Various embodiments of the invention will now be described by way of example only.

[0020] It is known in the prior art that thiols form coatings on metals. Thiols have also been used to tether species such as antibodies onto metal surfaces, for instance those of gold particles, for the purposes of immobilisation etc. One would expect that such coatings would also bind contaminants to the surface.

[0021] As much electrode chemistry involves interaction at the electrode surface, it is thus surprising that coatings used to bind molecules to the metal surface can be useful in preventing contamination of the electrode surface. It is also surprising that notwithstanding the application of the coating an electrode retains desirable electrochemical properties. The procedure for preparing the metal electrode stabilised by a coating involves contacting a metal electrode with selected sulphur-containing compounds, such as thiols, disulphides and compounds of the formula SO_(x) among others being suitable in the context of the present invention. The coatings also desirably contain a hydrophilic group which includes such species as hydroxyl, amino, carboxyl, carbonyl, oligo (ethylene oxide) chains and zwitterionic species. The latter two compounds indicate that compounds having one or more hydrophilic groups are also suitable groups for use in the present invention.

[0022] Between the sulphur group, which acts to tether the molecule onto the metal surface, and the hydrophilic group, which presents a hydrophilic surface, spacers may be employed.

[0023] Compounds useful in the present invention include, but are not limited to 2-mercaptoethanol, 2-mercaptoethylamine, 3-mercaptopropionic acid, thiophene, 4-carboxy thiophene, cysteine, homocysteine and cystine. Most preferably the molecule is cystine. In any of the above aspects, the D or L isomers can be used or mixtures of D and L isomers can be used, where such isomers are possible.

[0024] The compound in accordance with the invention is then applied as a monolayer or multilayer onto the surface of the electrode. It is possible to apply the compound by simply exposing the electrode to the coating material, with the coating material in either the vapour phase or in solution. The substance can be applied by dipping, spraying, painting, printing etc. After application, it is possible to wash the surface of the contacted electrode.

[0025] In a further aspect of the current invention the layer of the sulfur containing compound can optionally be overcoated with a surfactant layer. The surfactant layer can be applied after the application of the sulfur containing layer or at the same time as the sulfur containing layer, for example the sulfur containing species and the surfactant can be placed in a coating bath into which the electrode material is immersed. Due to the higher affinity of the sulfur containing species for the electrode material it will bind to the electrode surface in preference to the surfactant, leaving the surfactant in a layer over the sulfur containing layer An example of a suitable surfactant is Triton X-100.

EXAMPLES Example 1 Preparation

[0026] The electrode coatings were applied to gold or palladium electrodes by immersing the sheet of material from which the electrodes were made into a 1 mM aqueous solution of the coating compound adjusted to pH 12 by the addition of potassium hydroxide. The contact time between the electrode material and the coating bath was typically 30 seconds. After coating, the electrodes were washed by immersion in a bath of water. In some cases, the electrodes were immersed in a third bath containing 1,000 ppm of triton X-100 in water. Finally, the electrode material sheets were dried by blowing with air at room temperature.

Example 2 Storage

[0027] The data in Tables 1 and 2 below show the effect on the electrode stability of coating the electrodes with sulphur-containing compounds. The stability was assessed using an accelerated test. The glucose sensors using coated or uncoated electrodes were stored either at 4° C. in the refrigerator (“fridge” ) or at 56° C. in an oven for two weeks. The sensors stored at 4° C. do not change significantly from their performance when freshly prepared and tested. Those stored in the oven are subject to accelerated ageing, which simulates longer ageing times at room temperature.

Example 3 Testings

[0028] After two weeks the sensors were tested with whole blood samples with various glucose concentrations, from about 3 mM to 30 mM. The background ferrocyanide concentration was measured (the reading obtained when a sample contains no glucose) and. the overall precision and fill speed of the sensors was assessed. The effect of the electrode coatings is shown in Table 1. The fill speeds in Table 1 were assessed qualitatively by eye The fill speeds in Table 2 were assessed quantitatively by videoing the filling of the sensor with a blood sample using an on-screen timer and subsequently determining the number of seconds required for the blood to fill each sensor.

[0029] It can be seen from the first pair of results, for a non-coated electrode, that artificial ageing dramatically increased the % cv (corresponding to decreased precision).

[0030] In contrast, for the last two pairs of results, the % cv's for the treated electrodes after artificial ageing were comparable to the % cv's of untreated electrodes on fridge storage and significantly better than accelerated aged untreated electrodes.

[0031] A desirable side effect of the present invention also appears to be maintenance of good fill speed for sensors on ageing. TABLE 1 TEST DATA BACKGROUND MEAN FILL STORAGE COATING (mM ferrocyanide) % cv SPEED Fridge None 1.01 3.8 OK Oven None 5.12 10.05 very slow Fridge Cysteine 1.3  4.5 OK Oven Cysteine 5.0  8.0 slow Fridge Cysteine/trit 1.98 3.1 fast Oven Cysteine/trit 2.17 5.4 OK Fridge Homocysteine/ 1.02 4.6 OK trit Oven Homocysteine/ 2.34 4.2 faster than trit Cysteine/ trit Fridge Cystine/trit  0.63* 4.1 fast Oven Cystine/trit  1.24* 4.4 good

[0032] TABLE 2 PRECISE FILL TIMES FILL TIME STORAGE COATING (secs) Fridge none 1.0 Oven none 5.3 Fridge Cystine 0.4 Oven Cystine 4.0 Fridge Cystine/trit 0.3 Oven Cystine/trit 1.4

[0033] A person skilled in the art will appreciate that the application process is very simple and facile and could be accomplished from the teaching hereof in many ways. 

What is claimed is:
 1. A coated metal electrode, the metal electrode comprising a coating and an overcoating, wherein the overcoating comprises a surfactant, wherein the coating comprises a sulfur containing moiety in its molecular structure, and wherein a temporal stability of the coated metal electrode is greater than a temporal stability of a corresponding uncoated metal electrode.
 2. The coated metal electrode according to claim 1, wherein the sulfur containing moiety comprises a thiol.
 3. The coated metal electrode according to claim 1, wherein the sulfur containing moiety comprises a disulfide.
 4. The coated metal electrode according to claim 1, wherein the sulfur containing moiety comprises SO_(x).
 5. The coated metal electrode according to claim 1, wherein the sulfur containing moiety is incorporated in a cyclic structure.
 6. The coated metal electrode according to claim 1, wherein the coating further comprises a hydrophilic group.
 7. The coated metal electrode according to claim 6, wherein the hydrophilic group is selected from the group consisting of a hydroxyl group, an amine group, a carboxyl group, a carbonyl group, and an oligo(ethyleneoxide)chain group.
 8. The coated metal electrode according to claim 6, wherein the hydrophilic group comprises a zwitterionic species.
 9. The coated metal electrode according to claim 8, wherein the zwitterionic species comprises an amine group and a carboxyl group.
 10. The coated metal electrode according to claim 6, wherein the coating further comprises a spacer between the sulfur containing moiety and the hydrophilic group.
 11. The coated metal electrode according to claim 10, wherein the spacer comprises an alkyl group or an aromatic group.
 12. The coated metal electrode according to claim 11, wherein the alkyl group comprises at least one of a methylene group and an ethylene group.
 13. The coated metal electrode according to claim 1, wherein the coating further comprises a compound selected from the group consisting of 2-mercaptoethanol, 2-mercaptoethylamine, 3-mercaptopropionic acid, thiophene, cysteine, homocysteine, 3-carboxythiophene, and cystine.
 13. The coated metal electrode according to claim 12, wherein the compound is a stereospecific compound.
 14. The coated metal electrode according to claim 13, wherein the stereospecific compound comprises a mixture of D isomers and L isomers.
 14. The coated metal electrode according to claim 13, wherein the stereospecific compound comprises a D isomer.
 14. The coated metal electrode according to claim 13, wherein the stereospecific compound comprises an L isomer.
 16. A method of preparing a metal electrode stabilized by a coating, the method comprising: contacting a metal electrode with a substance comprising a sulfur containing moiety in its molecular structure; and thereafter contacting the metal electrode with a surfactant, whereby a coated metal electrode is obtained, wherein a temporal stability of the coated metal electrode is increased relative to that of a corresponding uncoated metal electrode.
 17. A method of sensing an analyte, the method comprising: contacting a sample comprising an analyte to a metal electrode, the metal electrode comprising a coating and an overcoating, wherein the overcoating comprises a surfactant, wherein the coating comprises a sulfur containing moiety in its molecular structure, and wherein a temporal stability of the coated metal electrode is greater than a temporal stability of a corresponding uncoated metal electrode; and obtaining a measurement indicative of a presence of the analyte in the sample. 